Methods and devices using group III nitride compound semiconductor

ABSTRACT

A layer comprising silicon oxide (SiO 2 ) is formed on (111) plane of a silicon (Si) substrate in a striped pattern which is longer in the [1-10] axis direction perpendicular to the [110] axis direction. Then a group III nitride compound semiconductor represented by a general formula Al x Ga y In 1−x−y N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) is laminated thereon. The group III nitride compound semiconductor represented by a general formula Al x Ga y In 1−x−y N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) grows epitaxially on the substrate-exposed regions B which are not covered by the SiO 2  layer, and grows epitaxially on the SiO 2  layer in lateral direction from the regions B. Consequently, a group III nitride compound semiconductor having no dislocations can be obtained.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention is directed to methods and devices using a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1). In particular, the present invention is directed to methods and devices using a group III nitride compound semiconductor which has a substrate comprising silicon (Si). A group III nitride compound semiconductor layer comprises binary compounds such as AlN, GaN, and InN. A group III nitride compound semiconductor layer also comprises ternary compounds such as Al_(x)Ga_(1−x)N, Al_(x)In_(1−x)N, and Ga_(x)In_(1−x)N (0<x<1). And a group III nitride compound semiconductor layer further comprises quaternary compounds such as Al_(x)Ga_(y)In_(1−x−y)N (0<x<1, 0<y<1, 0<x+y<1).

[0003] 2. Description of the Related Art

[0004] A group III nitride compound semiconductor is a direct-transition-type semiconductor having a wide emission spectrum range from ultraviolet to red, and is applied to light-emitting devices such as light-emitting diodes (LEDs) and laser diodes (LDs). Group III nitride compound semiconductors are, in general, formed on a sapphire substrate.

[0005] However, in the above-described conventional technique, when a layer of a group III nitride compound semiconductor is formed on a sapphire substrate, cracks and/or warpage may be generated in the semiconductor layer. These flaws form due to differences in thermal expansion coefficients between the sapphire substrate and the group III nitride compound semiconductor. As a consequence, dislocations are generated in the semiconductor layer due to misfit, resulting in degraded device characteristics. Further, because sapphire has an insulation characteristic, both positive and negative electrodes need to be formed on the same side of the sapphire substrate, resulting in limitation of miniaturizing the device and degraded manufacturing efficiency. Moreover, because the substrate and the semiconductor layer are made of different materials, the conventional laser diodes have difficulty in obtaining a good cleavage.

SUMMARY OF THE INVENTION

[0006] Accordingly, in light of the above problems, an object of the present invention is to realize an efficient method capable of forming a layer of a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) on a silicon substrate, thereby to improve device characteristics. Another object of the present invention is to obtain the optimum surface orientation of the silicon substrate and the optimum orientation for epitaxial growth when the layer of a group III nitride compound semiconductor is formed on the silicon substrate by using epitaxial growth.

[0007] In order to solve above and other problems, in a first aspect, the present invention is a device using a group III nitride compound semiconductor comprising: a silicon (Si) substrate; a layer which is formed on (111) plane of the silicon substrate such that substrate-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; and a second layer which grows epitaxially on substrate-exposed portions, or the regions which are not covered by the first layer, and which grows epitaxially on the regions which are covered by the first layer in lateral direction.

[0008] The lateral direction, as used in the specification, refers to a direction parallel to a surface of the substrate (surface direction). The second layer comprising a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) does not grow epitaxially on the first layer, and the layer formed on the substrate-exposed portions grows epitaxially on the first layer in lateral direction. Dislocations due to misfit between the silicon substrate and the group III nitride compound semiconductor grow in longitudinal direction, but they hardly grow in lateral direction. Consequently, a crystallinity of the group III nitride compound semiconductor formed on the first layer can be improved. In addition, since there are no chemical junctions between the first layer and the group III nitride compound semiconductor thereabove, the second layer causes neither warpage nor distortions which would otherwise be caused by stress in the layer.

[0009] In a second aspect, the present invention is a device using group III nitride compound semiconductor comprising: a silicon (Si) substrate; a first layer which is formed on (111) plane of the silicon substrate and made of a group III nitride compound semiconductor; a second layer which is formed on the first layer such that the first layer-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; and a third layer which grows epitaxially on the third layer-exposed portions, or the regions which are not covered by the second layer, and which grows epitaxially on the regions which are covered by the second layer in lateral direction.

[0010] The third layer comprising a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) is formed on an exposed portion of the first layer comprising a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1), which serves as a nucleus, as in the first aspect of the present invention. Because crystal growth of the third layer is carried out not on the silicon substrate but on a substrate having the same or similar compositions to those of the third layer, crystallinity of the third layer can be improved. Here similar compositions as used in the specification refers to close lattice constants. The reference also includes the difference of composition ratios of Al, Ga and In (including 0) in the group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1).

[0011] In a third aspect, the present invention forms the first layer to have two-layer structure, comprising a layer made of Al_(x)Ga_(1−x)N (0<x≦1) and a layer made of a group III nitride compound semiconductor formed thereabove. By forming the first layer, a group III nitride compound including aluminum (Al) can be formed on the silicon substrate in an excellent condition, and a group III nitride compound semiconductor of improved crystallinity can be obtained on the group III nitride compound semiconductor layer.

[0012] In a fourth aspect of the present invention, the first layer is formed in a striped pattern. In a fifth aspect of the present invention, the exposed portions formed on (111) plane of the silicon substrate or the upper surface of the third layer are longer in an axis direction which is perpendicular to <110> direction of the silicon substrate. In short, the first layer is formed so that the exposed portions become longer in a direction which is perpendicular to <110> direction of the silicon substrate. The second layer is formed on (111) plane of the substrate or on the third layer. Because the crystal structure of the second layer is affected by (111) plane of the silicon substrate, it can optimize the direction of epitaxial lateral growth of the second layer. Here <110> direction represents [110], [011] and [101] axes directions.

[0013] In a sixth aspect of the present invention, the first layer is formed using silicon oxide (SiO₂). In this case, the second layer is formed by using a group III nitride compound semiconductor which does not include aluminum (Al), and the second layer does not grow epitaxially on the first layer but grows epitaxially in lateral direction. As a result, crystallinity of the second layer can be improved.

[0014] In a seventh aspect of the present invention, the first layer is formed using metals of high husing point or an amorphous silicon (Si). Because the first layer has conduction characteristic, electric current can flow uniformly in perpendicular direction to the surface between the second layer and the silicon substrate when the silicon substrate has conduction characteristic. As a result, electrodes can be formed on the silicon substrate and on the group III nitride compound semiconductor, and the device can be miniaturized. Metals of high husing point refer to metals whose husing point is larger than 2000 Å, e.g., niobium (Nb), molybdenum (Mo), ruthenium (Ru), hafnium (Hf), tantalum (Ta), and tungsten (W).

[0015] In an eighth aspect, the present invention is a method for manufacturing the group III nitride compound semiconductor of the first to third aspects represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1). In a ninth aspect of the present invention, the method of the eighth aspect is repeated several times. In a tenth aspect, the present invention is a method for manufacturing the group III nitride compound semiconductor of the fourth and fifth aspects represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1). By using these various methods, a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) and having excellent crystallinity can be obtained.

[0016] A twelfth aspect of the present invention shows the same effect as in the sixth and seventh aspects of the present invention. A thirteenth aspect of the present invention is a wafer by removing at least silicon substrate among the silicon substrate, the third layer and the first layer. As a result, a single group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) can be obtained as a substrate.

[0017] Here layers in a striped pattern are not necessarily formed on the entire surface but can be formed where they are necessary. And length of the regions formed in a striped pattern to expose the silicon substrate or the third layer can be arbitrary. The silicon or the third layer-exposed portions can be formed in a length so as to cross the entire length of the substrate, or can be formed intermittently. And when the silicon or the third layer-exposed portions are connected to the regions which are not formed in a striped pattern and the regions which are formed in a striped pattern has only a small proportion of the entire surface, that is all included in the present embodiment.

[0018] Other objects, aspects and advantages of the invention will be apparent to those skilled in the art upon reading the specification and appended claims which, when read in conjunction with the accompanying drawings, explain the principles of this invention.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] The accompanying drawings, which constitute part of this specification, serve to elucidate the principles of this invention. In such drawings:

[0020]FIGS. 1A and 1B are sectional views showing a structure of a group III nitride compound semiconductor in accordance with a first embodiment of the present invention;

[0021]FIG. 2 is a schematic view showing a structure of a group III nitride compound semiconductor in accordance with a second embodiment of the present invention;

[0022]FIG. 3 is a schematic view showing a structure of a group III nitride compound semiconductor in accordance with a third embodiment of the present invention;

[0023]FIG. 4 is a schematic view of showing a structure of a group III nitride compound semiconductor in accordance with a fourth embodiment of the present invention;

[0024]FIGS. 5A and 5B are schematic views showing epitaxial lateral growth of the group III nitride compound semiconductor in accordance with the third embodiment of the present invention and epitaxial growth of a group III nitride compound semiconductor in accordance with a comparative example.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] The present invention will be described hereinbelow with reference to specific embodiments. These embodiments are not exclusive or exhaustive as to the scope of this invention. In FIGS. 1A-1B, 2-4, and 5A-5B, the Miller indices are represented by adding a bar over each of the numbers. In the specification, on the other hand, the Miller indices are represented by minus sign before the appropriate numbers. For example, three axes shown in FIGS. 1A-1B are described as [111], [1-10], and [11-2] in this specification.

[0026] A normal direction of the (111) plane of a silicon substrate is the [111] axis direction, and the [1-10] axis direction is perpendicular to the [110] axis direction on the (111) plane. The [11-2] axis direction is perpendicular to the [1-10] axis direction on the (111) plane. Accordingly, in FIGS. 1A-1B, 2-4, and 5A-5B, each of which illustrates structures of a semiconductor layer formed on the (111) plane by crystal growth, three axes of the silicon substrate are shown, namely the [111] axis, the [1-10] axis, and the [11-2] axis.

EXAMPLE 1

[0027] (First Embodiment)

[0028] FIGS. 1A-1B are schematic sectional views showing the structure of a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) according to a first embodiment of the present invention. On a silicon substrate 10, an SiO₂ layer (a first layer) 12 having a thickness of about 2000 Å is formed in a striped pattern (FIG. 1B). A GaN layer (a second layer) 14 having a thickness of about 10 μm is formed in regions B where the first layer 12 is removed from the silicon substrate 10 and in regions which are defined above the islands of the first layer 12.

[0029] Next, a process for manufacturing the group III nitride compound semiconductor according to an embodiment of the present invention will be described.

[0030] SiO₂ and the group III nitride compound semiconductor are formed through the use of a sputtering method and a metal organic vapor phase epitaxy (hereinafter referred to as “MOVPE”) method, respectively. Gases used in the MOVPE method are ammonia (NH₃), carrier gas (H₂, N₂), and trimethyl gallium (Ga(CH₃)₃) (hereinafter referred to as “TMG”)

[0031] First, a first layer 12 made of SiO₂, having a thickness about 2000 Å and a width a of about 5 m, is formed through sputtering in a striped pattern on a silicon substrate 10, having a principal plane of (111) and cleaned with aqueous hydrofluoric acid. As shown in FIG. 1A, each of the regions B where the substrate 10 was exposed had a width b of about 5 m. Boundary lines between the regions A (which are defined above the islands of the first layer 12) and regions B (where the first layer 12 is removed from the silicon substrate 10) are in the [1-10] axis direction, which is perpendicular to the <110> direction of the silicon substrate 10.

[0032] Then, a GaN layer having a thickness of about 10 m is grown in accordance with the MOVPE method, in which the substrate 10 was maintained at 1100° C., and N₂ or H₂ was fed at 20 liters/min, NH₃ at 10 liters/min, and TMG at 100 mol/min, thereby obtaining a second layer 14. In this case, the GaN layer grows on regions B where the substrate 10 is exposed, in perpendicular direction. In each of the regions A (which are defined above the islands of the first layer 12), GaN grows in a lateral direction, i.e., in a surface direction, from the GaN layer grown epitaxially on an exposed portion of the substrate 10, which serves as a nucleus. The second layer 14 will have dislocations along the perpendicular direction only in the regions B where the substrate 10 is exposed. When in the regions A (which are defined above the islands of the first layer 12), the GaN layer is grown epitaxially in a lateral direction, the GaN layer will have no dislocations therein. Since the area of the region A (which are defined above the islands of the first layer 12) is made larger than that of the region B (where the silicon substrate 10 is exposed), a second layer 14 made of GaN having excellent crystallinity can be formed over a wide area. In addition, since there are no chemical junctions between the first layer 12 and the GaN layer (the second layer 14) thereabove, warpage and stress-induced distortion in the second layer 14 can be significantly reduced.

[0033] Although in the above-described embodiment the regions A which are defined above the island of the first layer 12 are formed in a striped pattern has a width of about 5 m, a preferred range for the width a is 1 m to 10 m. This is because when the width a of the regions A becomes larger than 10 m, a longer time is required for the lateral growth, and when the width a of the regions A becomes smaller than 1 m, removing SiO₂ film by using, e.g., hydrofluorine (HF), becomes difficult.

[0034] Additionally, although the width b of the regions B where the substrate 10 is exposed is 5 μm in this embodiment, a preferred range for the width b is 1 μm to 10 m. This is because when the width b of the regions B becomes larger than 10 μm, the probability of generating dislocations increases, and when the width b of the regions B becomes smaller than 1 μm, obtaining a GaN film with wide area and high quality becomes difficult. Further, from the viewpoint of the crystallinity of the second layer 14, the ratio of the widths of regions A (which are defined above the first layer 12) to the width b (of the regions B where the silicon substrate 10 is exposed), i.e., a/b, is preferably within the range of 1 to 10.

EXAMPLE 2

[0035] (Second Embodiment)

[0036] In the first embodiment, the SiO₂ layer, the first layer 12, is formed on the silicon substrate 10. In this second embodiment, however, a first layer 16 made of a group III nitride compound semiconductor is formed on the silicon substrate 10. Then an SiO₂ layer 18 (corresponding to first layer 12 of the first embodiment) is formed on the first layer 16 in an island pattern, and a group III nitride compound semiconductor layer 20 is formed thereon.

[0037]FIG. 2 is a schematic sectional view showing the structure of a group III nitride compound semiconductor according to a second embodiment of the present invention. On a silicon substrate 10, an Al_(0.15)Ga_(0.85)N layer 16 (a first layer) having a thickness of about 1000 Å is uniformly formed. Next a second layer 18 made of SiO₂ and 2000 Å in thickness is formed on the first layer 16 in a striped pattern or a grid pattern, as with the first (SiO₂) layer 12 in the first embodiment. A GaN layer (a third layer) 20 having a thickness of about 10 μm is formed in regions B (where the second layer 18 is removed from the first layer 16) and in regions A (which are defined above the islands of the second layer 18).

[0038] Next, a process for manufacturing the group III nitride compound semiconductor according to the second embodiment of the present invention will be described.

[0039] While the substrate 10 is maintained at 1150° C., N₂ or H₂ is fed at 10 liters/min, NH₃ at 10 liters/min, TMG at 100 μmol/min, and trymethyl aluminum (Al(CH₃)₃) (hereinafter “TMA”) at 10 μmol/min, resulting in formation of an Al_(0.15)Ga_(0.85)N first layer 16 having a thickness of about 1000 Å.

[0040] Then, the second layer 18 made of SiO₂, having a thickness about 2000 Å and a width a of about 5 μm, is formed in a striped pattern on the first layer 16, and each of the regions B where the first layer 16 was exposed had a width b of about 5 μm, as in the first embodiment. Boundary lines between the regions A (which are defined above the islands of the second layer 18) and regions B (where the second layer 18 is removed from the first layer 16) are in the [1-10] axis direction, which is perpendicular to the <110> direction of the silicon substrate 10.

[0041] The third layer 20 made of GaN, having a thickness of about 10 m, is formed on the both regions of the second layer 18 and the regions B (where the first layer 16 is exposed, as with the first and second layers 12 and 14 in the first embodiment). In this case, the GaN layer grows in perpendicular direction on regions B where the first layer 16 was exposed, using Al_(0.15)Ga_(0.85)N of the exposed region B as nucleus. In each of the regions A (which are defined above the islands of the second layer 18), GaN grows in a lateral direction, from the GaN layer grown epitaxially on an exposed portion of the first layer 16, which serves as a nucleus. Accordingly, the third layer 20 made of GaN is formed on the second layer 18 and on the exposed regions of the first layer 16.

[0042] As described above, because the GaN layer grows on the Al_(0.15)Ga_(0.85)N layer first, crystallinity of the GaN layer formed on the Al_(0.15)Ga_(0.85)N layer improves compared with the GaN layer formed on the substrate 10. Further, by removing the silicon substrate 10 or the region C, which consists of layers from the silicon substrate 10 to the second layer 18, using polishing or etching, a group III nitride compound semiconductor substrate having no dislocations can be obtained from the third layer 20.

[0043] Although in the present embodiment the first layer 16 is formed of aluminum gallium nitride whose composition is represented as Al_(0.15)Ga_(0.85)N, there may be used a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) and having an arbitrary composition ratio. However, when a layer is formed epitaxially on the silicon substrate 10, Al_(x)Ga_(1−x)N (0<x≦1) (including AlN) is preferably used. In addition, as for the third layer 20, a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) and having an arbitrary composition ratio may be used. In this case, the composition ratio of the third layer 20 can or cannot be identical to that of the first layer 16.

[0044] In the present embodiment the first layer 16 has a thickness of about 1000 Å. When the first layer 16 has a thickness smaller than 100 Å, the speed of lateral overgrowth of the third layer 20 becomes smaller. So preferably, the first layer 16 has a thickness larger than 100 Å. Further preferably, the first layer 16 has a thickness larger than 500 Å.

EXAMPLE 3

[0045] (A Third Embodiment)

[0046] In the second embodiment, the first layer 16 has a single layer structure. However, in this third embodiment, the first layer 16 is formed to have double layer structure.

[0047]FIG. 3 is a schematic sectional view showing the structure of a group III nitride compound semiconductor according to a third embodiment of the present invention. On a silicon substrate 10, an Al_(0.15)Ga_(0.85)N layer 16 having a thickness of about 1000 Å is formed. A GaN layer 17 having a thickness of about 1000 Å is formed on the layer 16. Accordingly, a first layer consisting of the layers 16 and 17 is formed. On the layer 17, an SiO₂ layer (a second layer) 18 having a thickness of about 2000 Å is formed in a striped pattern or a grid pattern as with the SiO₂ layer 12 in the first embodiment. A GaN layer (a third layer) 20 having a thickness of about 10 m is formed on the layer 17 and the second layer 18.

[0048] Next, a process for manufacturing the group III nitride compound semiconductor will be described.

[0049] The layer 16 is formed on the substrate 10 using the MOVPE method as in the second embodiment.

[0050] While the substrate 10 was maintained at 1100° C., N₂ or H₂ is fed at 20 liters/min, NH₃ at 10 liters/min, and TMG at 200 μmol/min, resulting in formation of a GaN layer 17 having a thickness of about 1000 Å.

[0051] Then, the second layer 18 made of SiO₂, having a thickness about 2000 Å and a width a of about 5 m, is formed in a striped pattern and each of the regions B where the layer 17 was exposed had a width b of about 5 m, as in the first and second embodiments. Boundary lines between the regions A (which are defined above the islands of the second layer 18) and regions B (where the second layer 18) are removed from the layer 17 are in the [1-10] axis direction, which is perpendicular to the <110> direction of the silicon substrate 10.

[0052] The third layer 20 made of GaN, having a thickness of about 10 m, was formed on the second layer 18 and on the regions B where the layer 17 is exposed. In this case, the GaN layer grows in a perpendicular direction on regions B where the layer 17 is exposed, using GaN of the exposed region B as nucleus. In each of the regions A (which are defined above the islands of the second layer 18), the GaN layer grows in a lateral direction, from the GaN layer grown epitaxially on an exposed portion the layer 17, which serves as a nucleus. As a result, a GaN layer having improved crystallinity compared with those of the first and second embodiments can be obtained.

[0053] In the present (third) embodiment, the GaN substrate comprising the third layer 20 and having no dislocations can be obtained by polishing and etching to remove the silicon substrate 10 or the region C, which consists of layers from the silicon substrate 10 to the second layer 18, as in the second embodiment. In the present embodiment, the layer 17 and the third layer 20 are made of GaN. Alternatively, the layer 17 and the third layer 20 may be made of a group III nitride compound semiconductor represented by the formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1), having an identical composition. When SiO₂ is used for the second layer 18, a group III nitride compound semiconductor which does not contain Al is preferably used as the layer 17 and the third layer 20. As a matter of course, the compositions of a group III nitride compound semiconductor of the layer 17 may be rendered different from that of the third layer 20.

[0054]FIGS. 5A and 5B are schematic views showing a growing process according to embodiments of the present invention. In FIG. 5A, a GaN layer grows epitaxially in longitudinal and lateral directions according to the method of the present embodiment. The third layer 18 made of SiO₂ is formed in a striped pattern, which is longer in the [1-10] axis direction perpendicular to the <110> direction on the surface (111) of the silicon substrate 10. The third layer 20 made of GaN grows epitaxially in the [11-2] axis direction (lateral direction) in order to cover the upper surface of the second layer 18 made of SiO₂ more rapidly than in the [111] axis direction (longitudinal direction) which is perpendicular to the (111) plane.

[0055] As a comparative example, the second layer 18 made of SiO₂ is formed in a striped pattern, which is longer in the [11-2] axis direction, is laminated under the same conditions as that of the third embodiment. FIG. 5B is a schematic view showing the process of the comparative example. Although the third layer 20 made of GaN grows epitaxially in the [111] axis direction (longitudinal direction) which is perpendicular to the (111) plane, it hardly grows in the [11-2] axis direction (lateral direction) in order to cover the upper surface of the second layer 18 made of SiO₂.

EXAMPLE 4

[0056] (Fourth Embodiment)

[0057] This embodiment has multiple layers. A first layer and a second layer each have two-layer structure. The first layer consists of layers 21 and 22, and the second layer consists of a layers 31 and 32. The first layer and the second layer each formed on the layer 6 is represented by the “first” first layer 21 and the “first” second layer 31, respectively. The first layer and the second layer each formed on the “first” second and first layers 31 and 21 is represented by the “second” first layer 22 and the “second” second layer 32, respectively.

[0058] In the present embodiment, after the layer consisting of the layers 16 and 17, a second layer 21 of SiO₂ and a third layer 31 consisting of a GaN layer are laminated on the substrate, as with layers 18 and 20 in the third embodiment, another layer (a fourth layer) 22 of SiO₂ is formed. The fourth layer 22 covers the regions of the third layer 31 which are not covered by the second layer 21 of SiO₂. Then a GaN layer grows epitaxially in order to cover the entire surface of the layer 31 and the fourth layer 22. Accordingly, a fifth layer 32 of GaN is formed. As shown in FIG. 4, the second layer 21 of SiO₂ covers the regions A and does not cover the regions B, while the fourth layer 22 of SiO₂ covers the regions B and does not cover the regions A. As a result, the third layer 31 made of GaN grows epitaxially in the regions B (where the layer 17 is exposed), covers the second layer 21 of SiO₂ (also covers the regions A by lateral growth). And the fifth layer 32 grows epitaxially in the regions A where the layer 31 is exposed, and covers the fourth layer 22 of SiO₂ (and also covers the regions B by lateral growth). Even when a growth defect (e.g., a crack) from the (111) plane of the silicon substrate 10 remains, a possibility that the growth defect (crack) is transmitted to the layer 32 is quite small as shown by arrows of broken lines in FIG. 4. That is, a growth defect (crack) that may be transmitted rectilinear in the [111] axis direction is perfectly screened by the fourth layer 22. In the present invention, by polishing and etching to remove the region D in FIG. 4, a group III nitride compound semiconductor substrate having no dislocations can be obtained by the fifth layer 32.

[0059] In the above embodiments, the layers 14, 20, 31 and 32 are made of GaN. Alternatively, they can be made of an aluminum gallium indium nitride represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) and having an arbitrary composition ratio. However, because a group III nitride compound semiconductor including Al grows easily on an SiO₂ layer, a group III nitride compound semiconductor which does not include Al is preferably used.

[0060] In the embodiments, the layers 12, 18, 21 and 22 are formed in a striped pattern and are made of SiO₂. Alternatively, the layers 12, 18, 21 and 22 can be made of metals of high husing point such as tungsten (W) and amorphous silicon(Si). In case that the layers 12, 18, 21 and 22 comprise metals or amorphous silicon, electric current flows in the layers 12, 18, 21 and 22. As a result, electric current can flow more uniformly in thickness direction of the group III nitride compound semiconductor. When the layers 12, 18, 21 and 22 are made of metals of high husing point such as tungsten (W) and amorphous silicon(Si), a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N (0≦x≦1, 0≦y≦1, 0≦x+y≦1) and having an arbitrary composition ratio does not grow epitaxially on the layers 12, 18, 21 and 22. Thus a group III nitride compound semiconductor represented by a general formula Al_(x)Ga_(y)In_(1−x−y)N can be used to form those layers.

[0061] In the first to fourth embodiments, each layer can be formed after a buffer layer is formed on a substrate by growing a group III nitride compound semiconductor at low temperature.

[0062] Although in each of the embodiments described above the MOVPE method is performed under atmospheric pressure, the MOVPE method may be performed under a reduced pressure. Further, the MOVPE method may be performed under atmospheric pressure and a reduced pressure in combination.

[0063] The silicon substrate can be n-type, p-type or semi-insulating. For example, when the silicon substrate is formed to have n-type conduction, conduction type of the group III nitride compound semiconductor which grows on the substrate can be controlled by doping an n-type impurity such as silicon (Si) or germanium (Ge). And when the silicon substrate is not removed, the substrate preferably has an n-type or a p-type conduction.

[0064] The group III nitride compound semiconductor of the present invention can be used as a substrate of light-emitting devices such as LEDs and LDs. Also, the group III nitride compound semiconductor of the present invention can be used to light-receiving devices and electric devices. The group III nitride compound semiconductor can be used with the silicon substrate.

[0065] The foregoing detailed description of the preferred embodiments of the invention has been provided for the purpose of explaining the principles of the invention and its practical application, thereby enabling others skilled in the art to understand the invention for various embodiments and with various modifications as are suited to the particular use contemplated. The foregoing detailed description is not intended to be exhaustive or to limit the invention to the precise embodiments disclosed. Modifications and equivalents will be apparent to practitioners skilled in this art and are encompassed within the spirit and scope of the appended claims. 

What is claimed is:
 1. A group III nitride compound semiconductor comprising: a silicon (Si) substrate; a first layer which is formed on (111) plane of said silicon substrate such that substrate-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; and a second layer which grows epitaxially on substrate-exposed portions, or the regions which are not covered by said first layer, and which grows epitaxially on the regions which are covered by said first layer in lateral direction.
 2. A group III nitride compound semiconductor comprising: a silicon (Si) substrate; a first layer which is formed on (111) plane of said silicon substrate and made of a group III nitride compound semiconductor; a second layer which is formed on said first layer such that first layer-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; a third layer which grows epitaxially on said first layer-exposed portions, or the regions which are not covered by said second layer, and which grows epitaxially on the regions which are covered by said second layer in a lateral direction.
 3. A group III nitride compound semiconductor according to claim 2, wherein said first layer is formed to have two-layer structure, consisting of a layer made of Al_(x)Ga_(1−x)N (0<x≦1) and a layer made of a group III nitride compound semiconductor formed on said layer made of Al_(x)Ga_(1−x)N (0≦x≦1).
 4. A group III nitride compound semiconductor according to claim 1, wherein said first layer is formed in a striped pattern.
 5. A group III nitride compound semiconductor according to claim 2, wherein said second layer is formed in a striped pattern.
 6. A group III nitride compound semiconductor according to claim 1, wherein said exposed portions which are not covered by said first layer are longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 7. A group III nitride compound semiconductor according to claim 2, wherein said exposed portions which are not covered by said second layer are longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 8. A group III nitride compound semiconductor according to claim 1, wherein said first layer comprises silicon oxide (SiO₂).
 9. A group III nitride compound semiconductor according to claim 2, wherein said second layer comprises silicon oxide (SiO₂).
 10. A group III nitride compound semiconductor according to claim 1, wherein said first layer comprises metals of high husing point or an amorphous silicon (Si).
 11. A group III nitride compound semiconductor according to claim 2, wherein said second layer comprises metals of high husing point or an amorphous silicon (Si).
 12. A method for manufacturing a group III nitride compound semiconductor on a silicon (Si) substrate, comprising: forming a first layer on (111) plane of said silicon (Si) substrate such that substrate-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; growing a group III nitride compound semiconductor on the regions which are not covered by said first layer epitaxially; and growing a second layer made of a group III nitride compound semiconductor epitaxially on the regions which are covered by said first layer in lateral direction.
 13. A method for manufacturing a group III nitride compound semiconductor on a silicon (Si) substrate, comprising: forming a first layer on (111) plane of said silicon (Si) substrate such that substrate-exposed portions are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; forming a second layer made of a group III nitride compound semiconductor by growing epitaxially on substrate-exposed portions which are not covered by said first layer and growing epitaxially on the regions which are covered by said first layer in lateral direction; forming a third layer on said second layer so as to cover the regions which are not covered by said first layer; growing said third layer epitaxially on the regions of said second layer which are not covered by said third layer; and forming a fourth layer made of a group III nitride compound semiconductor by growing epitaxially on the regions which are covered by said third layer in lateral direction.
 14. A method for manufacturing a group III nitride compound semiconductor on a silicon (Si) substrate, comprising: forming a first layer comprising a group III nitride compound semiconductor on (111) plane of said silicon substrate; forming a second layer on said first layer such that exposed portions of said first layer are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; and forming a third layer made of a group III nitride compound semiconductor by growing epitaxially on said exposed portions of said first layer which are not covered by said second layer and growing epitaxially on the regions which are covered by said second layer in a lateral direction.
 15. A method for manufacturing a group III nitride compound semiconductor on a silicon (Si) substrate, comprising: forming a first layer comprising a group III nitride compound semiconductor on a (111) plane of said silicon substrate; forming a second layer on said fist layer such that exposed portions of said first layer are formed in a scattered manner and on which a group III nitride compound semiconductor does not grow epitaxially; forming a third layer made of a group III nitride compound semiconductor by growing epitaxially on said exposed portions of said first layer which are not covered by said second layer and growing epitaxially on the regions which are covered by said second layer in a lateral direction; forming a fourth layer on said third layer so as to cover the regions which are not covered by said second layer; growing said fourth layer epitaxially on the regions of said third layer which are not covered by said second layer; and forming a fifth layer made of said group III nitride compound semiconductor by growing epitaxially on the regions which are covered by said fourth layer in lateral direction.
 16. A method for manufacturing a group III nitride compound semiconductor according to claim 15, wherein said first layer is formed to have two-layer structure, consisting of a layer made of Al_(x)Ga_(1−x)N (0<x≦1) and a layer made of a group III nitride compound semiconductor formed on said layer made of Al_(x)Ga_(1−x)N (0<x≦1).
 17. A method for manufacturing a group III nitride compound semiconductor according to claim 12, wherein said first layer is formed in a striped pattern.
 18. A method for manufacturing a group III nitride compound semiconductor according to claim 13, wherein said first layer is formed in a striped pattern and wherein said third layer is formed in a striped pattern.
 19. A method for manufacturing a group III nitride compound semiconductor according to claim 14, wherein said second layer is formed in a striped pattern.
 20. A method for manufacturing a group III nitride compound semiconductor according to claim 15, wherein said second layer and said fourth layer are formed in striped patterns.
 21. A method for manufacturing a group III nitride compound semiconductor according to claim 12, wherein said exposed portions which are not covered by said first layer is longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 22. A method for manufacturing a group III nitride compound semiconductor according to claim 13, wherein said exposed portions which are not covered by said first layer is longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 23. A method for manufacturing a group III nitride compound semiconductor according to claim 14, wherein said exposed portions which are not covered by said second layer is longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 24. A method for manufacturing a group III nitride compound semiconductor according to claim 15, wherein said exposed portions which are not covered by said second layer is longer in an axis direction which is perpendicular to <110> direction of said silicon substrate.
 25. A method for manufacturing a group III nitride compound semiconductor according to claim 12, wherein said first layer comprises silicon oxide (SiO₂).
 26. A method for manufacturing a group III nitride compound semiconductor according to claim 13, wherein said first layer and said third layer comprises silicon oxide (SiO₂).
 27. A method for manufacturing a group III nitride compound semiconductor according to claim 14, wherein said second layer comprises silicon oxide (SiO₂).
 28. A method for manufacturing a group III nitride compound semiconductor according to claim 15, wherein said second and fourth layers comprise silicon oxide (SiO₂).
 29. A method for manufacturing a group III nitride compound semiconductor according to claim 12, wherein said first layer comprises metals of high husing point or an amorphous silicon (Si).
 30. A method for manufacturing a group III nitride compound semiconductor according to claim 13, wherein said first layer comprises metals of high husing point or an amorphous silicon (Si).
 31. A method for manufacturing a group III nitride compound semiconductor according to claim 14, wherein said second layer comprises metals of high husing point or an amorphous silicon (Si).
 32. A method for manufacturing a group III nitride compound semiconductor according to claim 15, wherein said second and fourth layers comprise metals of high husing point or an amorphous silicon (Si).
 33. A method for manufacturing a group III nitride compound semiconductor according to claim 12, further comprising a step of: forming a wafer consisting of a group III nitride compound semiconductor by removing at least silicon substrate among said silicon substrate, said third layer and said first layer.
 34. A method for manufacturing a group III nitride compound semiconductor according to claim 13, further comprising: forming a wafer consisting of a group III nitride compound semiconductor by removing at least silicon substrate among said silicon substrate, said third layer and said first layer.
 35. A method for manufacturing a group III nitride compound semiconductor according to claim 14, further comprising: forming a wafer consisting of a group III nitride compound semiconductor by removing at least silicon substrate among said silicon substrate, said first layer and said second layer.
 36. A method for manufacturing a group III nitride compound semiconductor according to claim 15, further comprising: forming a wafer consisting of a group III nitride compound semiconductor by removing at least silicon substrate among said silicon substrate, said first layer and said second layer. 